The influence of crosslinking and fumed silica nanoparticles on mixed gas transport properties of poly[1-(trimethylsilyl)-1-propyne]

Crosslinking poly[1-(trimethylsilyl)-1-propyne] (PTMSP) films with 3,3′-diazidodiphenylsulfone, a bis(azide) crosslinker, rendered the films insoluble in common solvents for PTMSP such as toluene. At all temperatures, mixed gas CH₄ and n-C₄H₁₀ permeabilities of crosslinked PTMSP were less than those of uncrosslinked PTMSP, which correlates with lower free volume in the crosslinked material. The presence of fumed silica (FS) nanoparticles in both uncrosslinked PTMSP and crosslinked PTMSP increased mixed gas CH₄ and n-C₄H₁₀ permeabilities, consistent with the disruption of polymer chain packing by such nanoparticles. Mixed gas CH₄ permeabilities of all films were significantly less than their corresponding pure gas CH₄ permeabilities. For example, at 35 °C, the mixed gas CH₄ permeabilities were approximately 60-80% less than their pure gas values. The greatest decrease was observed for uncrosslinked PTMSP, while nanocomposite PTMSP films showed the least decrease. The mixed gas n-C₄H₁₀/CH₄ selectivities of crosslinked PTMSP and nanocomposite PTMSP films were less than those of uncrosslinked PTMSP at all temperatures. For example, at 35 °C, the mixed gas n-C₄H₁₀/CH₄ selectivities of uncrosslinked PTMSP, crosslinked PTMSP containing 10 wt% crosslinker, and uncrosslinked PTMSP containing 30 wt% FS were 33, 27, and 17, respectively, when the feed gas contained 2 mol% n-C₄H₁₀ and the total upstream mixture fugacity was 11 atm. For all films, as temperature decreased, mixed gas n-C₄H₁₀ permeabilities increased, and mixed gas CH₄ permeabilities decreased. Consequently, the mixed gas n-C₄H₁₀/CH₄ selectivities increased substantially as temperature decreased and the mixed gas selectivity of uncrosslinked PTMSP increased from 33 to 170 as temperature decreased from 35 °C to -20 °C when the feed gas contained 2 mol% n-C₄H₁₀ and the total upstream mixture fugacity was 11 atm.