High-strength biodegradable poly(vinyl alcohol)/fly ash composite films

Dilip Chandra Deb Nath, Sri Bandyopadhyay, Philip Boughton, Aibing Yu, Daryl Blackburn, Chris White

Research output: Contribution to journalArticleResearchpeer-review

24 Citations (Scopus)

Abstract

We prepared biodegradable composite films of poly(vinyl alcohol) (PVA) and fly ash (FA) spanning 5, 10, 15, 20, and 25 wt concentrations by casting aqueous solutions. The tensile strengths of the composite films were increased proportionally via the addition of FA. The strength of the film was enhanced by 193 with 20 FA compared to the neat PVA control. Further addition of FA deviated from the linear trend. The moduli of the composites also increased proportionally with FA addition to 212 at 20 wt FA addition compared to the control. The percentage strain at break exponentially decreased with the addition of FA. In the dynamic mechanical behavior, the storage and loss moduli both increased with FA content. The tan d peaks corresponding to the glass-transition temperature shifted 5-10?C higher above the control sample (73?C). This shift was attributed to a reduction in the mobility of PVA segments because they were anchored by the FA surface. The reductions in mobility manifested in strong interfacial interactions were indicative of hydrogen bonding. Broadening and reduction in the intensities of the stretching and bending peaks of -OH, -CH and -C=O of PVA in the Fourier transform infrared spectra were observed. This suggested that hydrogen bonding was active between the functional groups in the FA and PVA chains.
Original languageEnglish
Pages (from-to)114 - 121
Number of pages8
JournalJournal of Applied Polymer Science
Volume117
Issue number1
DOIs
Publication statusPublished - 2010
Externally publishedYes

Cite this