Comparative study of 1,2-dichlorethane decomposition over Ni-based catalysts with formation of filamentous carbon

Yurii I. Bauman, Ilya V. Mishakov, Denis V. Korneev, Yury V. Shubin, Aleksey A. Vedyagin, Roman A. Buyanov

Research output: Contribution to journalArticleResearchpeer-review

10 Citations (Scopus)


Catalytic chemical vapor deposition of 1,2-dichlorethane over Ni-based catalysts into carbon nanostructured materials was studied. The catalysts were prepared by mechanochemical activation and by metal dusting of bulk nickel-containing alloy precursors. Model Ni-M alloys, where M is Co, Cu, and Fe, were obtained by coprecipitation technique. Loading of M in the samples was varied in a range of 1–5 at.%. Pure nickel was used a reference. The kinetics of carbon deposition was investigated using flow reactor equipped with McBain balances. The samples of carbon product were characterized by nitrogen adsorption, scanning and transmission electron microscopies. The hydrogen addition into reaction mixture was shown to have opposite effect on both catalytic behavior and carbon yield depending on catalyst's nature. Segmented structure of carbon filaments formed specifies its developed surface area. Both bulk chlorination of nickel particles and its blockage by dense carbon deposits in the case of mechanochemically prepared samples were suggested to be responsible for rapid deactivation of the catalyst.

Original languageEnglish
Pages (from-to)147-152
Number of pages6
JournalCatalysis Today
Publication statusPublished - 1 Mar 2018
Externally publishedYes


  • Carbon nanomaterials
  • CCVD
  • Mechanochemical activation
  • Metal dusting
  • Nickel alloys
  • Segmented structure

Cite this